Q: A customer has asked whether we can supply carbon and alloy steel valve bodies meeting Supplemental Requirement S23 in ASTM A What is the. fication, shall apply to steel castings for pressure-containing Specification A and SI units for material ordered to parts under each of the following ASTM. Buy ASTM A /AM: SPECIFICATION FOR STEEL CASTINGS, GENERAL REQUIREMENTS, FOR PRESSURE-CONTAINING.

Author: Moogubar Fautaur
Country: Mauritius
Language: English (Spanish)
Genre: Medical
Published (Last): 5 July 2010
Pages: 360
PDF File Size: 9.23 Mb
ePub File Size: 3.50 Mb
ISBN: 280-9-95135-813-7
Downloads: 60386
Price: Free* [*Free Regsitration Required]
Uploader: Tygonos

If fracture occurs, it has a rock-candy appearance due to fracture along the prior austenite grain boundaries. ViewIn Technology for Mechanical Seals.

This specification covers steel castings, general requirements, for pressure-containing parts. The thickness of the casting orportion of the casting is an obviousfactor influencing whether embrittlementoccurs, since thicker casting sectionswill cool more slowly through thecritical temperature range than thinsections.

Monitoring Pressure Relief Devices Post: Latest Post Popular Links Events.

Standard Specification for Steel Castings, General Requirements, for Pressure-Containing Parts

Texas Manufacturing Expands Modestly, Outlook. The resulting etched specimen is compared with 10 reference macrographs.

Looking asm a career in the Valve Industry? Although some foundries monitor nitrogen levels in their steel, many do not have the necessary equipment to do this.

Admiral Valve Announces Partnership with Diek. Stainless Steel, for Pressure-Containing Parts. New Washer Application Search Tool. These are provided for use when additional testing or inspection is desired and apply only when specified individually by the purchaser in the order. The mechanical test methods and definitions are presented in details.

TOP Related  LOBULILLO HEPATICO PDF

Supplemental Requirement S23 in ASTM A

What is the purpose of this requirement? Most foundries have the equipment necessary to analyze and report aluminum content. In order to avoid castings with q703 gas porosity, the foundry may add deoxidizing elements to the melt.

The fracture is often very shiny due to the presence of aluminum nitride platelets on the surface. For heats with aluminum content greater than 0. This compound tends to precipitate in the prior austenite grain boundaries and can result in castings that display loss of ductility that could result in brittle failure of the casting if it is shock-loaded in service.

Historical Version s – view previous versions of standard. New Products Prev Next Rotork: The mold material can also influence the cooling rate. Emerson Completes Acquisition of iSolutions Inc.

Rigging and Lifting of Large Valves Post: One of the elements that is sometimes added as a deoxidizer is aluminum, which creates a potential for the formation of aluminum nitride. The steel shall be made by open-hearth or electric-furnace process, z703 or without separate refining such as argon-oxygen-decarburization AODunless otherwise designated by the individual specification.

TOP Related  IEC 60909-4 PDF

When steel is melted, oxygen and nitrogen can be dissolved in the molten steel. Steel Castings, Ferritic and Martensitic, for Pressure. For example, air-set sand is known to inherently produce molds that cool slower than green-sand molds. This abstract is a brief summary of the referenced standard.

A cross-section of the heaviest section of a sacrificial casting A coupon attached to the heaviest section A coupon removed from directly under a riser or A coupon from the same heat of material removed from a separately cast test block with a thickness representative of the heaviest section of the casting. Steel Castings, Martensitic Stainless atsm Alloy, for.

Therefore, the nitrogen content of the steel is often not known or reported, and it is possible that enough nitrogen is present to form aluminum nitride.

The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other.

An analysis of each heat shall be made by the manufacturer to determine the percentages of the elements specified.